Scalable deposition of MASnI2Br-based perovskite solar cells via ultrasonic spray pyrolysis

ALDEMİR D. A., Lapa H. E., Şen E., KALELİ M.

Modern Physics Letters B, cilt.38, sa.29, 2024 (SCI-Expanded, Scopus) identifier

  • Yayın Türü: Makale / Tam Makale
  • Cilt numarası: 38 Sayı: 29
  • Basım Tarihi: 2024
  • Doi Numarası: 10.1142/s0217984924502749
  • Dergi Adı: Modern Physics Letters B
  • Derginin Tarandığı İndeksler: Science Citation Index Expanded (SCI-EXPANDED), Scopus
  • Anahtar Kelimeler: large-area, perovskite solar cells, Tin-based perovskite, ultrasonic spray pyrolysis
  • Isparta Uygulamalı Bilimler Üniversitesi Adresli: Hayır

Özet

All layers of MASnI2Br-based perovskite solar cells (PSCs) were deposited by ultrasonic spray pyrolysis method. The depositions of the layers were carried out in a large area. The perovskite thin film deposited on FTO/TiO2 had large grains. The crystallite size of the film was calculated as 90 nm from the XRD pattern. The bandgap of 1.54 eV was determined from the UV-visible measurement of MASnI2Br thin film. The PSCs with the different active areas (0.3 cm2 and 3.18 cm2Þ were fabricated. The champion cells' power conversion efficiencies were recorded at 0.181% and 0.120% for 0.3 cm2 and 3.18 cm2, respectively.