The effect of boronizing on the magnetization behaviour of low carbon microalloyed steels
Journal of Magnetics, vol.17, no.2, pp.96-99, 2012 (SCI-Expanded, Scopus)
- Publication Type: Article / Article
- Volume: 17 Issue: 2
- Publication Date: 2012
- Doi Number: 10.4283/jmag.2012.17.2.096
- Journal Name: Journal of Magnetics
- Journal Indexes: Science Citation Index Expanded (SCI-EXPANDED), Scopus
- Page Numbers: pp.96-99
- Keywords: Boronizing, Coatings, Iron boride, Saturation magnetization, X-ray diffraction
- Open Archive Collection: AVESIS Open Access Collection
- Isparta University of Applied Sciences Affiliated: No
Abstract
The change of saturation magnetization in boronized low carbon microalloyed steels was investigated as a function of boronizing time. Specimens were boronized in an electrical resistance furnace for times ranging from 3 to 9 h at 1123 K. The metallurgical and magnetic properties of the specimens were investigated using optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD) and vibrating sample magnetometry (VSM). A boride layer with saw-tooth morphology consisting of FeB and Fe 2B was observed on the surface, its thickness ranged from 63 μm to 140 μm depending on the boronizing time. XRD confirmed the presence of Fe 2B and FeB on the surface. The saturation magnetization decreased with increasing boronizing time. This decrease was attributed to the increased thickness of the FeB and Fe 2B phases. Cracks were observed at the FeB/Fe 2B interfaces of the samples. The number of interfacial cracks increased with increasing boronizing time. © 2012 Journal of Magnetics.